Sensors are essential components in modern industry and daily life, and platinum electrodes, as one of the core materials of sensors, play a crucial role in the performance and stability of sensors. In the preparation of sensor electrodes,
Platinum electrode slurryThe selection and use are also crucial steps. This article will introduce a platinum electrode slurry launched by Advanced Institute Technology, as well as its characteristics, process, and superior performance indicators.
1、 Characteristics of Advanced Institute Technology Platinum Electrode Slurry
Advanced Institute Technology Platinum Electrode Slurry (brand XJY-YB-8840) is a uniformly colored black paste. It has outstanding performance indicators of fineness ≤ 15 μ m, viscosity Pa • s of 60-80, and solid content of 80 ± 1. The testing conditions for viscosity are BROOK FINED DV-II, 52 #, 1rpm, 25 ℃.
In the process of preparing sensor electrodes, Advanced Institute Technology's platinum electrode slurry has coating or printing characteristics, which can be easily applied to different preparation processes, making the sensor preparation process more convenient and efficient.
2、 Recommended Process for Advanced Institute Technology Platinum Electrode Slurry
In order to achieve the best preparation effect, Advanced Institute Technology provides users with a recommended set of process steps:
1. Printing process: Use 300 mesh nylon or stainless steel wire mesh for the printing process. After printing, it is recommended to lay the printed result flat for 3 minutes to achieve better leveling effect.
2. Drying temperature: You can choose an infrared lamp or a 150 ℃ oven for drying. This can quickly evaporate the solvent in the slurry, making the electrode surface smoother.
3. Sintering temperature: The recommended sintering temperature range is 850~1200 ℃. During the sintering process, it is recommended to set a peak holding time of 10 minutes, and the optimal sintering cycle is 45-60 minutes. This can ensure that the platinum electrode is fully cured and grain grows after sintering, improving its performance.
3、 Technical indicators of sintered platinum electrode slurry from Advanced Institute of Technology
After using advanced technology platinum electrode slurry for preparation, the following excellent technical indicators can be obtained:
1. Excellent adhesion: Advanced Institute Technology's platinum electrode slurry has good adhesion, which can ensure a strong bond between the electrode and the substrate, enhance the stability and service life of the sensor.
2. Low square resistance: After sintering, the square resistance of the platinum electrode can be controlled within the range of 20 ± 5m Ω/□. This low square resistance can effectively improve the sensitivity and response speed of the sensor.
Summary:
Advanced Institute of Technology Platinum Electrode SlurryWith its excellent performance indicators and easy to operate process flow, it has become an ideal choice for preparing high-performance sensor electrodes. Through the introduction of this article, it is believed that readers have gained a deeper understanding of Advanced Institute Technology's platinum electrode slurry. I hope this advanced technology product can play a greater role in the field of sensors, promoting the continuous upgrading and innovation of sensor technology.