Silver platinum conductor paste has a wide sintering temperature range, resistance to silver ion migration, and extraordinary welding resistance on alumina substrates. It can be used as a substitute for gold platinum paste in some applications

Gold conductor pasteIt is composed of high-purity ultrafine gold powder, inorganic binder, and organic carrier. Gold conductor paste is a necessary material for thick film multilayer systems sintered in the atmosphere. By screen printing on the top, bottom, or middle layers, thin, dense, and highly conductive conductors are formed between multiple layers of wiring. It can also be used for drawing lines on sensor element electrodes and soldering APM leads. Gold conductor paste not only has excellent printing performance, but also has excellent hot press welding and corrosion resistance. Used for hybrid integrated circuits, gas sensors, explosion-proof devices, etc.

Main advantages:
1. Good conductivity
2. High resolution of fine lines
3. The effective coverage area of the slurry is high
Slurry characteristics：
1. Appearance: brownish yellow paste like
2. Viscosity: 350-700 Pa · s (Brookfield viscometer DV II pro, 52 axis, 0.5rpm, 25 ℃)
3. Solid content: 84-88%;
4. Fineness:< 15μm；．
5. Dilution: This product is ready to use and can be used without the need for diluent. If dilution is required, please use turpentine alcohol and add no more than 5% by weight.
Film burning performance:
1. Film thickness during firing: 8-12 μ m;
2. Square obstruction:< 5m Ω/□ (film thickness 8-12mm);
3. Resolution:< 0.10mm
4. Coverage: 73cm2/g/9 μ m
5. Ultrasonic aluminum wire welding and hot pressed gold wire welding: 108mN
usage method:
1. Matrix: Aluminum oxide matrix
2. Screen printing: 325-400 mesh screen printing, also dot coating or drawing.
3. Mixing and application: Mix evenly before use.
4. Film formation process (recommended):
5. Leveling: After printing, please let it stand in a clean environment at room temperature (25 ℃) for 15 minutes;
6. Drying conditions: 110~135 ℃, 30 minutes;
7. Sintering conditions: 850-930 ℃, tunnel furnace for 60 minutes, peak value for 10 minutes.

Storage:
1. Storage stability: stored at room temperature in original sealed packaging for six months.
2. Packaging specifications: 10g, 50g, 100g
matters needing attention:
1. Safe use:wine of the best qualityContaining organic solvents, good ventilation should be maintained during use to avoid excessive steam inhalation into the body; If the slurry is accidentally swallowed, inhaled, or in contact with the skin, it is harmful. Therefore, it should be thoroughly cleaned immediately after use and avoid contact with eyes, skin, or clothing; Do not approach fire or combustibles as they are flammable.
2. This slurry is a ready to use product and does not need to be diluted. If dilution is required, the amount added should not exceed 5% (weight ratio). Excessive diluent will directly affect the performance of the slurry.
3. This slurry should be stored in a cool and dry place between 4-25 ℃.